PA66 A 30 S FN31 000000德國朗盛Durethan無鹵阻燃聚酰胺66尼龍塑料（18024445500）

PA 66, non-reinforced, injection molding, halogen free flame retardant, improved flowability



ISO Shortname: ISO1874-PA 66, GFHR, 12-040; ISO 1043 PA FR (30)

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 270 °C / WZ 80 °C; 600 bar % ISO 294-4 1.1　
C Molding shrinkage, transverse 60x60x2; 270 °C / WZ 80 °C; 600 bar % ISO 294-4 1.1　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.1　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.1　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 3800 1500
C Yield stress 50 mm/min MPa ISO 527-1,-2 85 50
C Yield strain 50 mm/min % ISO 527-1,-2 4.1 >20
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 60 N
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 50 80
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA <10 <10
Izod impact strength 23 °C kJ/m² ISO 180-1U 55 N
Izod impact strength -30 °C kJ/m² ISO 180-1U 55 60
Izod notched impact strength　kJ/m² ISO 180-1A <10 <10
Flexural modulus 2 mm/min MPa ISO 178-A 3700 1600
Flexural strength 2 mm/min MPa ISO 178-A 125 55
Flexural strain at flexural strength 2 mm/min % ISO 178-A 5.8 7,8
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 120 40

Thermal properties
C Melting temperature 10 °C/min °C ISO 11357-1,-3 265　
C Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 80　
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 212　
Vicat softening temperature 50 N; 120 °C/h °C ISO 306 230　
C Coefficient of linear thermal expansion, parallel 23 to 55 °C 10-4/K ISO 11359-1,-2 0.8　
C Coefficient of linear thermal expansion, transverse 23 to 55 °C 10-4/K ISO 11359-1,-2 0.7　
Burning behavior UL 94 0.4 mm Class UL 94 V-0　
C Oxygen index Method A % ISO 4589-2 34　
Glow wire test (GWFI) 0.4 mm °C IEC 60695-2-12 960　
Glow wire test (GWIT) 0.4 mm °C IEC 60695-2-13 775　

Electrical properties (23 °C/50 % r. h.)
C Relative permittivity 100 Hz - IEC 60250 4.0 8.0
C Relative permittivity 1 MHz - IEC 60250 4.0 4.0
C Dissipation factor 100 Hz 10-4 IEC 60250 120 2000
C Dissipation factor 1 MHz 10-4 IEC 60250 190 550
C Volume resistivity　Ohm·m IEC 60093 1E12 1E11
C Surface resistivity　Ohm IEC 60093 1E15 1E13
C Electric strength 1 mm kV/mm IEC 60243-1 30 25
C Comparative tracking index CTI Solution A V IEC 60112 600　

Other properties (23 °C)
C Density　kg/m³ ISO 1183 1169　

Processing conditions for test specimens
C Injection molding-Melt temperature　°C ISO 294 260　
C Injection molding-Mold temperature　°C ISO 294 80　

Processing recommendations
Drying temperature dry air dryer　°C - 80　
Drying time dry air dryer　h - 2-6　
Residual moisture content　% Acc. to Karl Fischer　0.03-0.07　
Melt temperature (Tmin - Tmax)　°C - 260-270　
Mold temperature　°C - 80-100　

C These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.